Fatigue(nlme)
Fatigue()所属R语言包：nlme
Cracks caused by metal fatigue
由金属疲劳引起的裂缝
译者：生物统计家园网 机器人LoveR
描述----------Description----------
The Fatigue data frame has 262 rows and 3 columns.
Fatigue数据框有262行，3列。
格式----------Format----------
This data frame contains the following columns:
这个数据框包含下列资料：
an ordered factor with levels 1 < 2 < 3 < 4 < 5 < 6 < 7 < 8 < 9 < 10 < 11 < 12 < 13 < 14 < 15 < 16 < 17 < 18 < 19 < 20 < 21 giving the test path (or test unit) number. The order is in terms of increasing failure time or decreasing terminal crack length.
同级别的有序因子1<2<3<4<5<6<<X ><7<8<9<10<11<12<13 <14<15<16<17<18<19<20测试路径（或试验单位）的数量。顺序是故障时间增加或减少终端裂纹长度。
number of test cycles at which the measurement is made (millions of cycles).
测试测量（百万次）周期数。
relative crack length (dimensionless).
相对裂纹长度（无量纲）。
Details
详情----------Details----------
These data are given in Lu and Meeker (1993) where they state “We obtained the data in Table 1 visually from figure 4.5.2 on page 242 of Bogdanoff and Kozin (1985).” The data represent the growth of cracks in metal for 21 test units. An initial notch of length 0.90 inches was made on each unit which then was subjected to several thousand test cycles. After every 10,000 test cycles the crack length was measured. Testing was stopped if the crack length exceeded 1.60 inches, defined as a failure, or at 120,000 cycles.
这些数据都路和米克（1993），他们的状态，“我们得到表1中，直观地从图4.5.2 Bogdanoff和Kozin（1985）第242页上的数据。”数据代表的裂纹增长21个试验装置的金属。当时受到数千名测试周期的每个单位一个长度为0.90英寸的初始缺口。每10,000个测试周期后，裂纹长度进行了测量。如果裂纹长度超过1.60英寸，定义为失败，或为12万次，测试停止。
源----------Source----------
Lu, C. Joseph , and Meeker, William Q. (1993), Using degradation measures to estimate a time-to-failure distribution, Technometrics, 35, 161-174
约瑟夫·鲁，C，和米克，威廉问：（1993），使用退化的措施，估计故障时间分布，Technometrics，35，161-174
转载请注明:出自 生物统计家园网(http://www.biostatistic.net)。